LEXAN™ 945 resin
Polycarbonate
SABIC Innovative Plastics
产品说明：
LEXAN 945 Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating and is available in various opaque color options. LEXAN 945 is a general purpose resin designed to meet the needs of various applications.
物性信息：
| 基本信息 |
|
| 黄卡编号 |
- E121562-220906
- E121562-100305095
|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| 外观 |
|
| 加工方法 |
|
| 多点数据 |
- Coefficient of Thermal Expansion vs. Temperature (ASTM E831)
- Flexural DMA (ASTM D4065)
- Pressure-Volume-Temperature (PVT - Zoller Method)
- Shear DMA (ASTM D4065)
- Specific Heat vs. Temperature (ASTM D3417)
- Tensile Fatigue
- Tensile Stress vs. Strain (ASTM D638)
- Thermal Conductivity vs. Temperature (ASTM E1530)
- Viscosity vs. Shear Rate (ASTM D3835)
|
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 比重 |
1.19 |
g/cm³ |
ASTM D792 |
| 熔流率（熔体流动速率） (300°C/1.2 kg) |
10 |
g/10 min |
ASTM D1238 |
| 收缩率 - 流动 (3.20 mm) |
0.60 到 0.80 |
% |
内部方法 |
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 拉伸模量 1 |
2280 |
MPa |
ASTM D638 |
| 抗张强度 2 |
|
|
ASTM D638 |
| 屈服 |
62.1 |
MPa |
ASTM D638 |
| 断裂 |
65.5 |
MPa |
ASTM D638 |
| 伸长率 3 |
|
|
ASTM D638 |
| 屈服 |
6.0 |
% |
ASTM D638 |
| 断裂 |
130 |
% |
ASTM D638 |
| 弯曲模量 4(50.0 mm 跨距) |
2340 |
MPa |
ASTM D790 |
| 弯曲强度 5(屈服, 50.0 mm 跨距) |
101 |
MPa |
ASTM D790 |
| 冲击性能 |
额定值 |
单位制 |
测试方法 |
| 悬壁梁缺口冲击强度 (23°C) |
800 |
J/m |
ASTM D256 |
| 装有测量仪表的落镖冲击 (23°C, Total Energy) |
73.4 |
J |
ASTM D3763 |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 载荷下热变形温度 |
|
|
ASTM D648 |
| 0.45 MPa, 未退火, 3.20 mm |
138 |
°C |
ASTM D648 |
| 1.8 MPa, 未退火, 3.20 mm |
127 |
°C |
ASTM D648 |
| 维卡软化温度 |
143 |
°C |
ASTM D1525 6 |
| 线形热膨胀系数 |
|
|
ASTM E831 |
| 流动 : -40 到 40°C |
6.7E-5 |
cm/cm/°C |
ASTM E831 |
| 横向 : -40 到 40°C |
6.7E-5 |
cm/cm/°C |
ASTM E831 |
| RTI Elec |
130 |
°C |
UL 746 |
| RTI Imp |
120 |
°C |
UL 746 |
| RTI |
130 |
°C |
UL 746 |
| 电气性能 |
额定值 |
单位制 |
测试方法 |
| 耐电弧性 7 |
PLC 7 |
|
ASTM D495 |
| 相比耐漏电起痕指数(CTI) |
PLC 2 |
|
UL 746 |
| 高电弧燃烧指数(HAI) |
PLC 3 |
|
UL 746 |
| 高电压电弧起痕速率 (HVTR) |
PLC 4 |
|
UL 746 |
| 热丝引燃 (HWI) |
PLC 2 |
|
UL 746 |
| 可燃性 |
额定值 |
单位制 |
测试方法 |
| UL 阻燃等级 |
|
|
UL 94 |
| 0.800 mm |
V-2 |
|
UL 94 |
| 1.14 mm |
V-0 |
|
UL 94 |
| 3.05 mm |
5VA |
|
UL 94 |
| 灼热丝易燃指数 (1.00 mm) |
960 |
°C |
IEC 60695-2-12 |
| 热灯丝点火温度 (1.00 mm) |
875 |
°C |
IEC 60695-2-13 |
| 极限氧指数 |
35 |
% |
ISO 4589-2 |
| 注射 |
额定值 |
单位制 |
|
| 干燥温度 |
121 |
°C |
|
| 干燥时间 |
3.0 到 4.0 |
hr |
|
| 干燥时间，最大 |
48 |
hr |
|
| 建议的最大水分含量 |
0.020 |
% |
|
| 建议注射量 |
40 到 60 |
% |
|
| 料筒后部温度 |
271 到 293 |
°C |
|
| 料筒中部温度 |
282 到 304 |
°C |
|
| 料筒前部温度 |
293 到 316 |
°C |
|
| 射嘴温度 |
288 到 310 |
°C |
|
| 加工（熔体）温度 |
293 到 316 |
°C |
|
| 模具温度 |
71.1 到 93.3 |
°C |
|
| 背压 |
0.345 到 0.689 |
MPa |
|
| 螺杆转速 |
40 到 70 |
rpm |
|
| 排气孔深度 |
0.025 到 0.076 |
mm |
|
| 备注 |
| 1 . |
50 mm/min |
| 2 . |
类型 1, 50 mm/min |
| 3 . |
类型 1, 50 mm/min |
| 4 . |
1.3 mm/min |
| 5 . |
1.3 mm/min |
| 6 . |
标准 B (120°C/h), 载荷2 (50N) |
| 7 . |
钨电极 |