CYCOLOY™ C2950 resin
Polycarbonate + ABS
SABIC Innovative Plastics
产品说明：
Non-chlorinated and non-brominated flame retardant PC/ABS offering balanced flow and impact plus improved heat resistance intended for various applications.
物性信息：
| 基本信息 |
|
| 黄卡编号 |
|
| 添加剂 |
|
| 特性 |
- Chlorine Free
- 抗撞击性，良好
- 良好的流动性
- 耐热性，中等
- 无溴
- 阻燃性
|
| 加工方法 |
|
| 多点数据 |
- Coefficient of Thermal Expansion vs. Temperature (ASTM E831)
- Elastic Modulus vs Temperature (ASTM D4065)
- Flexural DMA (ASTM D4065)
- Instrumented Impact (Energy) (ASTM D3763)
- Instrumented Impact (Load) (ASTM D3763)
- Pressure-Volume-Temperature (PVT - Zoller Method)
- Shear DMA (ASTM D4065)
- Specific Heat vs. Temperature (ASTM D3417)
- Tensile Creep (ASTM D2990)
- Tensile Fatigue
- Tensile Stress vs. Strain (ASTM D638)
- Thermal Conductivity vs. Temperature (ASTM E1530)
- Viscosity vs. Shear Rate (ASTM D3835)
|
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 比重 |
|
|
ASTM D792 |
| -- |
1.18 |
g/cm³ |
ASTM D792 |
| -- 1 |
1.22 |
g/cm³ |
ASTM D792 |
| 熔流率（熔体流动速率） (260°C/2.16 kg) |
10 |
g/10 min |
ASTM D1238 |
| 收缩率 |
|
|
内部方法 |
| 流动 : 3.20 mm |
0.40 到 0.60 |
% |
内部方法 |
| 横向流动 : 3.20 mm |
0.40 到 0.60 |
% |
内部方法 |
| 吸水率 |
|
|
ASTM D570 |
| 24 hr |
0.10 |
% |
ASTM D570 |
| 平衡, 23°C |
0.40 |
% |
ASTM D570 |
| 硬度 |
额定值 |
单位制 |
测试方法 |
| 洛氏硬度 (R 级) |
123 |
|
ASTM D785 |
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 抗张强度 2(屈服) |
62.7 |
MPa |
ASTM D638 |
| 伸长率 3(断裂) |
40 |
% |
ASTM D638 |
| 弯曲模量 4(100 mm 跨距) |
2650 |
MPa |
ASTM D790 |
| 弯曲强度 5(屈服, 100 mm 跨距) |
102 |
MPa |
ASTM D790 |
| 冲击性能 |
额定值 |
单位制 |
测试方法 |
| 悬壁梁缺口冲击强度 |
|
|
ASTM D256 |
| -30°C |
160 |
J/m |
ASTM D256 |
| 23°C |
530 |
J/m |
ASTM D256 |
| 装有测量仪表的落镖冲击 |
|
|
ASTM D3763 |
| -30°C, Total Energy |
54.2 |
J |
ASTM D3763 |
| 23°C, Total Energy |
61.0 |
J |
ASTM D3763 |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 载荷下热变形温度 |
|
|
ASTM D648 |
| 0.45 MPa, 未退火, 6.40 mm |
104 |
°C |
ASTM D648 |
| 1.8 MPa, 未退火, 3.20 mm |
90.6 |
°C |
ASTM D648 |
| 1.8 MPa, 未退火, 6.40 mm |
95.0 |
°C |
ASTM D648 |
| 维卡软化温度 |
113 |
°C |
ASTM D1525 6 |
| 线形热膨胀系数 |
|
|
ASTM D696 |
| 流动 : -30 到 30°C |
7.2E-5 |
cm/cm/°C |
ASTM D696 |
| 横向 : -30 到 30°C |
7.2E-5 |
cm/cm/°C |
ASTM D696 |
| 导热系数 |
0.20 |
W/m/K |
ASTM C177 |
| RTI Elec |
85.0 |
°C |
UL 746 |
| RTI Imp |
85.0 |
°C |
UL 746 |
| RTI |
85.0 |
°C |
UL 746 |
| 电气性能 |
额定值 |
单位制 |
测试方法 |
| 表面电阻率 |
> 1.0E+16 |
ohms |
ASTM D257 |
| 体积电阻率 |
1.0E+17 |
ohms·cm |
ASTM D257 |
| 介电强度 (3.20 mm, in Oil) |
19 |
kV/mm |
ASTM D149 |
| 介电常数 |
|
|
ASTM D150 |
| 50 Hz |
3.00 |
|
ASTM D150 |
| 60 Hz |
3.00 |
|
ASTM D150 |
| 100 Hz |
3.00 |
|
ASTM D150 |
| 耗散因数 |
|
|
ASTM D150 |
| 50 Hz |
5.0E-3 |
|
ASTM D150 |
| 60 Hz |
5.0E-3 |
|
ASTM D150 |
| 100 Hz |
4.9E-3 |
|
ASTM D150 |
| 耐电弧性 7 |
PLC 6 |
|
ASTM D495 |
| 相比耐漏电起痕指数(CTI) |
PLC 1 |
|
UL 746 |
| 高电弧燃烧指数(HAI) |
PLC 0 |
|
UL 746 |
| 高电压电弧起痕速率 (HVTR) |
PLC 2 |
|
UL 746 |
| 热丝引燃 (HWI) |
PLC 1 |
|
UL 746 |
| 可燃性 |
额定值 |
单位制 |
测试方法 |
| UL 阻燃等级 |
|
|
UL 94 |
| 1.50 mm |
V-0 |
|
UL 94 |
| 2.49 mm |
5VB |
|
UL 94 |
| 极限氧指数 |
32 |
% |
ASTM D2863 |
| 注射 |
额定值 |
单位制 |
|
| 干燥温度 |
82.0 到 88.0 |
°C |
|
| 干燥时间 |
3.0 到 4.0 |
hr |
|
| 干燥时间，最大 |
8.0 |
hr |
|
| 建议的最大水分含量 |
0.040 |
% |
|
| 建议注射量 |
30 到 80 |
% |
|
| 料筒后部温度 |
221 到 254 |
°C |
|
| 料筒中部温度 |
221 到 277 |
°C |
|
| 料筒前部温度 |
243 到 277 |
°C |
|
| 射嘴温度 |
243 到 277 |
°C |
|
| 加工（熔体）温度 |
243 到 277 |
°C |
|
| 模具温度 |
60.0 到 82.0 |
°C |
|
| 背压 |
0.345 到 0.689 |
MPa |
|
| 螺杆转速 |
40 到 70 |
rpm |
|
| 排气孔深度 |
0.038 到 0.076 |
mm |
|
| 备注 |
| 1 . |
Color |
| 2 . |
类型 1, 50 mm/min |
| 3 . |
类型 1, 50 mm/min |
| 4 . |
2.6 mm/min |
| 5 . |
2.6 mm/min |
| 6 . |
标准 B (120°C/h), 载荷2 (50N) |